Home

Hot-dip galvanized steel coil

Hot-dip galvanized sheets have a smooth and attractive surface, widely used in pre-coated base plates, construction, household appliances, automobiles, container manufacturing, and other industries.

Category:

Galvanized Steel Sheet

+86-18554320750

andylee0429@outlook.com

Inquiry

Back

Galvanized (Aluminum) Zinc Sheet

Galvanized Steel Coil is a zinc-coated steel sheet, mainly processing alkali and degreasing, acid bath, flux bath, anneal treatment, molten zinc dip, spangle-making, chromate treatment, oiling and other stages.

● Hot dip galvanized steel to prevent corrosion of steel surfaces subjected to extend its service life, in a layer of metal zinc coated steel surface, so that it improved the surface characteristics of thin steel plate.

● Hot-dip galvanizing is cold rolled strip steel by the formation, after annealing into the continuous hot galvanizing line, through a series of processes, surface hot-dip galvanized to form. Galvanized steel plate was good at corrosion resistance and high strength, easy processing and so on.

Product Specifications

Technical Standards	JIS 3302/GB 2518/EN10143
Grade	DX51D+Z, SGCC
Width	750-1250mm
Thickness	0.13-0.8mm
Zinc Coating	40g — 200g/sqm
ID Coil	508mm or 610mm

Item		Nominal Size (mm)
Nominal Thickness		0.1-1.5
Nominal Thickness	Steel Plate and Steel Strip	500-1250
Nominal Thickness	Longitudinally Cut Steel Strip	<600
Nominal Length	Steel Plate	1000-8000
Nominal Length	Steel Strip and Longitudinally Cut Steel Strip	610 or 508

Coating Structure Category

Classification Item	Category	Code
Coating Type	Zinc Coating	Z
	Zinc-Iron Alloy Coating	ZF
Coating Style	Uniform Thickness Coating A (g/m ² ) / B (g/m ² )(A=B)	A/B
	Different Thickness Coating A (g/m ² ) / B (g/m ² )(A≠B)
By negotiation between supplier and buyer, the code for equal thickness coating can be represented by the sum of both weights, where A is the coating weight on the outer surface of the steel strip or steel plate (g/m ² ); B is the coating weight on the inner surface of the steel strip or the underside of the steel plate (g/m ² ).